The galvanomagnetic Van der Pau measurements have been carried out on monocrystalline Cd HgTe (MCT) samples and epitaxial Cd HgTe/ CdZn Te (MCT/CZT) heterostructures ( x » 0,2) at T = 295 K and T = 77 K. The sample along with the cryostat rotated in magnetic field of electromagnet by (0-360°) - angle with 6-degree step. Angular dependencies of measured signal for p -type monocrystalline sample at T = 77 K were shown to be sinusoidal, hence, Hall coefficient did not depend upon magnetic field induction. However, for epitaxial MCT/CZT- heterostructures at T = 77 K measured signal angular dependencies differed greatly from sinusoids.
1. Белов А.Г., Белогорохов А.И., Лакеенков В.М. // Об особенностях электрофизиче-ских свойств гетероструктур CdxHg1xTe/CdZnTe // Физика и техника полупроводников. 2001. Т. 35. – № 8. С. 917919.
2. Исследование зависимостей проводимости и коэффициента Холла от магнитного поля в пленках CdxHg1xTe, выращенных методом молекулярно-лучевой эпитаксии» / П.А. Бахтин, С.А. Дворецкий, В.С. Варавин и др. // Физика и техника полупроводников. 2004. Т. 38. – № 10. С. 1203–1206.
3. Влияние низкотемпературного отжига на электрофизические параметры пленок n-CdHgTe / П.А. Бахтин, С.А. Дворецкий, В.С. Варавин и др. // Физика и техника полу-проводников. 2004. Т. 38. – №10. С. 1207–1210.
4. О влиянии медленных электронов на полевые зависимости коэффициента Холла для твердых растворов CdxHg1xTe при Т = 77К / А.Г. Белов, И.М. Белова, В.Е. Каневский и др. // Физика и техника полупроводников. 2007. Т. 41. – №10. С. 1178–1181.
5. Белов А.Г., Белова И.М., Каневский В.Е. // Разработка математической модели для описания полевых зависимостей коэффициента Холла для твердых растворов CdxHg1xTe при Т = 77К // Изв. МГИУ. Информационные технологии. 2007. №1. С. 9–13.
6. Елизаров А.И., Богобоящий В.В., Белов А.Г. // Вольт-амперные характеристики потенциальных барьеров в гетероструктурах CdxHg1xTe/CdTe // ФТП. 1990. Т. 24. – № 5. С. 923–926.